Enable
to compact super fine powder
Achive
high sintered density equal to or higher than MIM
Stable
and high flowability powder
Enable
to compact hard materials
|
![]() |
Materials | Particle Grades |
Original Powder |
Granulated Powder | Green Properties | Sintered Properties | |||||
---|---|---|---|---|---|---|---|---|---|---|
D50 (µm) |
D50 (µm) |
AD (g/cm3) |
FR (sec./50g) |
Green Density (%)∗1 |
Radial Crushing Strength (MPa)∗2 |
Sintered Temp. (°) |
Sintered Density (%) |
Shrinkage (%) |
||
316L | SC1308 | 7.0 | 70 | 2 | 27 | 79.6 | 7.5 | 1250 | 97.7 | 6.6 |
HK-30 | SC1008 | 6.1 | 73.0 | 7.6 | 1280 | 97.9 | 8.9 | |||
SC2008 | 9.7 | 74.7 | 6.5 | 1300 | 98.0 | 8.2 | ||||
SKD-11 | SC2008 | 10.3 | 71.9 | 5.6 | 1230 | 99.3 | 10.6 |
∗1:Compact Pressure:6t/cm2(588MPa)
∗2:Measured according to 「JIS Z 2507」
![]() |
![]() |
![]() |
∗ Micro-gear